Irradiance adjustment system developed for various types of solar cells and illumination conditions

Abstract

A new irradiance adjustment system for the light source named “Programmable Reference cell system for Irradiance adjustment by Spectral Measurement (PRISM)” has been developed for photovoltaics evaluation. It can be applied for various kinds of solar cells and illumination conditions without the preparation of conventional reference cells. This system consists of a device for absolute spectral responsivity measurements, that is, the spectral responsivity unit, and a device for irradiance adjustment of the light source, that is, the spectral reference cell. First, the short circuit current of the target solar cell (I_ref) is calculated by convolution of the absolute spectral responsivity with the spectral irradiance under STC (AM1.5 G, 1 kW/m², 25°C) as defined in IEC 60904-3. The spectral irradiance of the light source is then adjusted for I–V measurements so that the short-circuit current of the spectral reference cell (I_cal), calculated by convolution of the absolute spectral responsivity with the spectral irradiance of the light source, agrees with I_ref. The difference between I_ref and the short circuit current, as determined at an internationally recognized test center under STC, was within ±2% for crystalline silicon solar cells and ±3% for organic solar cells. The difference between I_cal and the short-circuit current measured under a solar simulator or LED in which the irradiance was adjusted by this system was within ±4% when the irradiance was higher than 4 W/m².

Introduction

Crystalline silicon solar cells are used in the largest quantities for solar energy systems, however, their high manufacturing cost and heavy weight prevent the widespread use of solar energy. To address this problem, various types of solar cells, for example, compound semiconductors, organic thin films, dye-sensitized, and perovskite [1] solar cells are under investigation by various groups with some of them being already commercialized.

Further development of materials and cell structure as well as appropriate evaluation methods for cell functions will be required to gauge and improve the overall performance of solar cells. International standards for the evaluation of silicon solar cells have been established by the IEC as the 60904 Series, however, they define only test methods under standard test conditions (STC) although, when compared to crystalline silicon-based cells, higher performance can be expected for some types of solar cells under weak irradiation such as faint morning, evening, indoor or oblique light [2]. Moreover, new types of solar cells sometimes have characteristics different from that of silicon solar cells such as nonlinearity between the current and light intensity, a light soaking effect, and slow response time, which are not taken into consideration in the IEC 60904 standards [3, 4].

The reference cell method is widely used for irradiance adjustment of a solar simulator [5] and this method requires the preparation of a reference cell as defined in IEC 60904-2, 4 [6, 7]. However, preparation of a reference cell with a spectral response that matches the solar cell being tested is difficult and extremely time-consuming [8, 9], especially, for such unstable cells as dye-sensitized solar cells (DSCs). It is necessary to prepare a filtered reference cell with its relative spectral responsivity coincident with that of the organic PV to be tested, which should then be calibrated at a recognized institute. However, this may take several months to 1 year since the filtered reference cell must also be checked for long-term stability. In this work, we have developed a new irradiance adjustment system for the light source named, “Programmable Reference cell system for Irradiance adjustment by Spectral Measurement (PRISM)” which can be applied for any type of solar cell under various illumination conditions without the use of conventional reference cells [10-19]. In this work, the performance of this system has been investigated for various solar cells and illumination conditions.

Principle

Basic procedures

The PRISM system consists of a device for absolute spectral responsivity measurements (spectral responsivity unit: SK-1150) which meets IEC 60904-4, 8 standards [7, 8] and a device for light source irradiance adjustment (spectral reference cell: SRC-1100), as shown in Figure 1. The basic procedures for measurements at STC (AM1.5G, 1 kW/m², 25°C) are as follows:

Figure 1. Schematic diagram of the PRISM system. PRISM, Programmable Reference cell system for Irradiance adjustment by Spectral Measurement.

1. Spectral responsivity of the target solar cell (S(λ)) is measured with the SK-1150 unit.
2. The short-circuit current of the target solar cell (I_ref) is calculated by convolution of the absolute spectral responsivity S(λ) with the spectral irradiance at STC (AM1.5G, 1 kW/m², 25°C) as defined in IEC 60904-3 (E_AM1.5G(λ)) [9], using the SRC-1100 reference cell device, as follows:

   Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): I_{ref}=\int S\left(\lambda \right)\cdot E_{AM1.5G}\quad \left(\lambda \right)\quad d\lambda

   (1)

3. The spectral irradiance of the solar simulator (E_ss(λ)) is adjusted until the short-circuit current of SRC-1100 (I_cal), calculated from equation (2), agrees with I_ref.

   Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): I_{cal}=\int S\left(\lambda \right)\cdot E_{SS}\quad \left(\lambda \right)\quad d\lambda

   (2)

4. Current-voltage characteristics (I–V curves) of the target cell are measured by a solar simulator, the irradiance of which is adjusted through the above procedures.

Measurement of nonlinear cells

The short-circuit current of some types of organic solar cells is not always proportional to the irradiance. In this case, equation (1) should be modified to

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): I_{ref}=\int S\left(\lambda ,E_b\right)\cdot E_{AM1.5G}\quad \left(\lambda \right)\quad d\lambda ,

(3)

where S(λ, E_b) indicates the spectral responsivity which may vary with the irradiance (E_b = ∫E_ss(λ) dλ). However, it is difficult to measure S(λ, E_b) by commonly available devices since they are not able to regulate the irradiance level to desired values. To address this problem, we have developed the PRISM system which uses the differential spectral responsivity (DSR) method developed by Physikalisch-Technische Bundesanstalt (PTB) and defined in IEC 60904-4, 8 and ISO 15387 [7, 8, 20, 21].

Measurements under various illumination conditions

The PRISM system employing the DSR method can be applied for measurements under any illumination conditions. Thus, the short-circuit current (I_sc) for any solar cell under any illumination conditions can be calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): I_{sc}=\int S\left(\lambda ,E_b\right)\cdot E\left(\lambda \right)\quad d\lambda ,

(4)

where E(λ) is the spectral irradiation from any light source.

Key Devices for the PRISM System

Spectral responsivity unit (SK-1150)

The SK-1150 unit has been constructed to simultaneously illuminate the bias light irradiance (E_b) and monochromatic light irradiance onto a solar cell. Both lights are combined in the lens and irradiated on the solar cell. The irradiation unit consists of a halogen lamp, Xenon lamp, grating and chopping units, and light monitors to compensate for any instability of the lamps. The current measurement unit consists of a source meter and lock-in amplifier, both of which are controlled by a computer.

The absolute spectral responsivity of this device is measured using a standard detector calibrated at an internationally recognized test center. Differential spectral responsivity is measured at various irradiances of bias light and S(λ, E_b) is then automatically calculated by a computer [7, 8, 20, 21].

When the current response to the applied light irradiation is slow, for example, in the case of dye-sensitized solar cells (DSCs), the chopping frequency of the monochromatic light should be low enough to obtain a steady-state current. Aoki et al. have reported that S(λ, E_b) decreases as the chopping frequency is increased [3], indicating that it should be lower than 3.3 Hz to obtain accurate data under 1 sun bias light irradiation. However, spectral responsivity measurement using the lock-in amplifier is unsuitable for low-frequency measurements since long and repetitive measurements are required to obtain accurate data, for example, several hours at 0.3 Hz.

To address this problem, this system has two methods to determine S(λ, E_b), that is, the selective amplification of the current caused by monochromatic light irradiation using the lock-in amplifier and the calculation of the difference between currents measured when the shutter of the monochromatic light is open and closed using the DC current amplifier. The latter method is similar to the AC-a method reported by Guo et al. [22], and requires less measuring time because the lock-in amplifier method takes a chopping frequency of 10 cycles.

Spectral reference cell device (SRC-1100)

The SRC-1100 device consists of a spectroradiometer for spectral irradiance measurement of the light source, an optical receiver and computer. With this device, irradiance adjustment of the solar simulator can be performed according to the procedures described in the 'Basic procedures' section.

The spectroradiometer equipped in this device has a high sensitivity image sensor of back-thinned CCD to measure very low irradiance, such as indoor light, as compared to AM 1.5 G (1 kW/m²). Additionally, it has a unique optical system to reduce stray light which causes inaccurate readings. Figure 2 shows the transmittance level of the stray light measured in accordance with JIS Z8724 (Japan Industrial Standards, Methods of measurement Light-source colour) [23].

Figure 2. Transmittance level of stray light determined for: (A) a conventional spectroradiometer; and (B) the spectroradiometer equipped in this device.

The irradiance measured by the spectroradiometer should have a linear relationship with the short-circuit current of the linear cell under a wide irradiation range, for example, from indoor light to 1 sun. The short-circuit current (I_sc) and linearity error (ε) were determined for the linear cell (Konica Minolta, AK-200) by the spectroradiometer and were plotted against the Irradiance (Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): {\textstyle \int E_{ss}\left(\lambda \right)d\lambda } ), as shown in Figure 3 (Konica Minolta is hereafter referred to as KM). The ε was calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \epsilon =(I_{sc}/I_{mes}-1)\times 100,

(5)

where Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): {\textstyle I_{sc}=\int S\left(\lambda \right)\cdot E_{ss}\left(\lambda \right)\quad d\lambda .}

Figure 3. Short-circuit current (Isc) and linearity error (ε) of SRC-1100 plotted against the irradiance. SRC, spectral reference cell

The linearity error (ε) was within ±0.2% at an irradiation range of 10–1000 W/m², as shown in Figure 3.

The sensitivity of a spectroradiometer is known to change with time [24] by vibration and degradation of its optical components, etc., while instrument-to-instrument variations also exist [25, 26]. No change in the relative spectral responsivity of the standard lamp was measured, but about a 5% decrease in irradiance was measured by the spectroradiometer in 100 days.

The SRC-1100 is first calibrated at the manufacturing factory using a standard lamp traceable to that of a recognized national institute; however, as mentioned above, the measured value changes with time. To reduce these effects, SRC-1100 has a user calibration function to resolve changes before measurements. This apparatus has a stable reference cell (KM, AK-200) with absolute spectral responsivity (S_rc(λ)) traceable to the calibrated value of a national institute. First, the reference cell is placed under the light source and the short-circuit current (I_{mes_rc}) is measured. Next, the irradiance (E_ss(λ)) is measured and the absolute irradiance calculated by multiplying (E_ss(λ)) by a correcting factor (K = I_{mes_rc}/E_ss(λ)·S_rc(λ)d λ). If the sensitivity of SRC-1100 shows no change with time, K equals 1.

Intercomparison of Short Circuit Currents Among Calibration Centers

Intercomparisons of the short circuit currents were carried out at three internationally recognized calibration centers, that is, the National Institute of Advanced Industrial Science & Technology (AIST), National Renewable Energy Laboratory (NREL), and PTB [27] for multiple reference cells (KM, AK series) to investigate variations in their measured values. Table 1 and Figure 4 show the type of cells in the AK series and their relative spectral responsivities, respectively. Table 1 also summarizes the centroid wavelengths (W_c) of the reference cells for the AK series which were calculated by equation (7). Here, it should be noted that W_c is the representative wavelength of the spectral responsivity at STC.

Table 1. Types of reference cells

Reference cells	Type	Centroid wavelength
DSC, dye-sensitized solar cells.
AK-100	Amorphous Si-type	521 nm
AK-110	Microcrystalline Si-type	791 nm
AK-120	Top layer of triple junction	499 nm
AK-130	Middle layer of triple junction	664 nm
AK-140	Bottom layer of triple junction	831 nm
AK-200	Crystalline Si-type	772 nm
AK-300	DSC N719 type	553 nm

Figure 4. Relative spectral responsivities of the reference cells.

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): W_c=\int S(\lambda )\cdot \lambda d\lambda \quad /\quad \int S(\lambda )\quad d\lambda .

(6)

The centroid wavelength can be employed as the index of each reference cell to indicate the representative spectral responsivity, thus, allowing comparisons of multiple reference cells. For example, the centroid wavelengths of AK-100 (Amorphous Si-type cell), AK-200 (Crystalline Si-type cell), and AK-110 (Microcrystalline Si-type cell) are 521 nm, 772 nm, and 791 nm, respectively. First, the short-circuit current of each cell was measured at KM, then the secondary reference solar cell was calibrated at AIST. The cells were then sent to PTB and NREL, and variations in the short circuit currents among the three recognized calibration centers were investigated. The difference in short-circuit current with the elapse of time was found to be within ±0.3% in a 2-year period from 2011 to 2013.

Figure 5 shows the differences in the short-circuit current among the test centers (ΔI_{sc_tc}) plotted against the centroid wavelength of the spectral responsivity (W_c) for each cell. The ΔI_{sc_tc} were calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \Delta {I_{sc}}_{\_tc}=\left(I_{sc\_tc}/I_{sc\_km}-\right. Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \left. 1\right)\times 100,

(7)

Figure 5. Difference in the short-circuit current among the calibration centers plotted against the centroid wavelength.

where I_{sc_tc} is the short-circuit current determined at PTB or NREL, and I_{sc_km} is that determined at KM with the secondary reference solar cell calibrated at AIST. Dirnberger et al. have reported intercomparison of the short-circuit current for crystal Si-type and amorphous Si-type modules performed by the Fraunhofer Institute for Solar Energy Systems (ISE), European Solar Test Installation (ESTI of the European Commission, Joint Research Centre, Institute for Energy and Transport, Renewable Energy Unit), and the NREL and AIST [28]. They reported that deviations in the short-circuit current of the crystal Si-type module was 2% (−1.1 to 0.9%), but that of the amorphous Si-type module was −2.9% for the data measured at AIST and 1.6% for that measured at NREL. The value from NREL was found to be 4.5% higher than that of AIST. In this paper, deviation of the short-circuit current was 0.9% for crystalline Si-type cells and 2.8% (0–2.8%) for amorphous Si-type cells. Thus, the value from NREL was 2.8% higher than that of AIST. The tendency for greater deviation of the short-circuit current for amorphous Si-type cells than crystalline Si-type cells was also recognized in this paper. As shown in Figure 5, the ΔI_{sc_tc} values of cells having W_c in the long wavelength range were negative and those of cells having W_c in the short wavelength range were positive, although the reason for this tendency is not yet clear at present. Further investigation is required to analyze this tendency. On the other hand, intercomparison results of this paper were found to be reasonable since the total estimated uncertainty to determine the short-circuit current was 3.8%. The estimated uncertainty of a recognized calibration center was within 1% and within 1.8% at KM. Taking these results into consideration, the maximum deviation under STC for the PRISM system was set within 4%, equivalent to the error range allowance in the above results.

Experimental

Performance verification of SK-1150

The performance of the SK-1150 unit was verified by comparing the short circuit currents of the solar cells at STC with those determined at a recognized test center. That is, the difference in the short-circuit current (ΔI_{sc_stc}) between that determined by SK-1150 (I_ref) and that determined at a test center (I_{ref_tc}) was calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \Delta I_{sc\_stc}=\left(I_{ref}/I_{ref\_tc}-1\right)\times 100.

(8)

Performance verification of SRC-1100

Performance of the SRC-1100 device was verified by comparing the short circuit currents calculated from equation (2) (I_cal) with those measured under a solar simulator (I_mes) or LED. The difference in the short-circuit current between I_cal and I_mes (ΔI_sc) was calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \Delta I_{sc}=\left(I_{cal}/I_{mes}-1\right)\times 100.

(9)

The three types of solar simulators and LED light source used in the evaluations are shown in Table 2. The solar simulators were all class AAA but with differing spectral irradiance distributions in order to examine the spectral irradiance dependence. The source meters were Agilent B2901A, ADCMT 6242, and Advantest R6246.

Table 2. Solar simulators and LED light source

Type	Manufacturer	Irradiance level	Target cells
DSC-NIMS-1, dye-sensitized solar cells-National Institute for Materials Science; OPV, organic thin film solar cell.
XES-40S	SAN-EI ELECTRIC	10–1000 W/m2	Reference cells/Nonlinear cells/DSC-NIMS/OPV
94023A	NewPort	1000 W/m2	Reference cells
YSS-T150A	YamashitaDenso	10–1000 W/m2	DSC-A/DSC-B
LED	Imac	10–300 W/m2	Reference cells/Nonlinear cells/DSC-NIMS/OPV

Spectral responsivity measurements of DSC

Two different types of dye-sensitized solar cells (DSCs) were tested: one cell containing 3-Methoxypropionitrile (MPN) as the solvent for the electrolyte (DSC-A) and the other containing an ionic liquid electrolyte (DSC-B). The viscosity of the ionic liquid electrolyte was about 30 times higher than that containing MPN at 20°C. A mesoscopic TiO₂ semiconductor electrode sensitized by cis-RuLL'-(SCN)₂ (L = 2,2′-bipyridyl-4,4′-dicarboxylic acid, L' = 4,4′-dinonyl-2,2′-bipyridyl) (Z907) dye was used for both cells. The active area for each cell was 0.196 cm² [3]. Additionally, DSCs supplied by the National Institute for Materials Science (DSC-NIMS-1 and DSC-NIMS-2) were also used. For these DSCs, a carbazole dye with hexyl-substituted oligothiophenes, MK-2 (Soken Chemical & Engineering Co., Ltd., Tokyo, Japan), was used as a sensitizer. An ionic liquid based on imidazolium iodide was used as the electrolyte. Transparent nanocrystalline TiO₂ films were prepared as follows: The films were formed by a screen printing method, that is, TiO₂ paste (Nanoxide-20N, Nikki Syokubai Kasei) was screen-printed onto a transparent conducting oxide (TCO) glass substrate (F-doped SnO₂, sheet resistance 10 ohm/cm², Nippon Sheet Glass), followed by sintering at 500°C for 60 min in air.

Before measurements, the cells were stabilized by light soaking at the same irradiance as that for the bias light. In the case of DSC-NIMS-1, the short-circuit current reached a steady-state value in about 96 h during light soaking at an irradiance of 1 sun. The cell was kept in the dark for about 100 h after 96 h light soaking, and then irradiated again under the same conditions. The short-circuit current reached a steady-state value immediately after irradiation.

The absolute spectral responsivity (S(λ)) was measured by SK-1150 at 25°C with bias light irradiance levels between 0 to 1.2 sun. Wavelength resolution was 10 nm and the chopping frequency of the monochromatic light was set low enough to obtain a steady-state current.

I–V measurements

Solar cell efficiencies are, at present, measured at STC, however, by adjusting the light irradiance using the PRISM method, I–V characteristics were measured under various irradiances with a solar simulator (San-ei Electric XES-40S) and LED light source (Imac). The voltage sweep rates were set so that an I–V curve determined by the forward scan (from short circuit to open circuit) agreed with that by reverse scan. The solar cell efficiency (η) and fill factor (FF) were calculated as follows:

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): \eta =\frac{V_{oc}\times J_{sc}\times FF}{P_{rad}}\times 100,

(10)

Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): FF=\frac{P_{max}}{V_{oc}\times J_{sc}},

(11)

where V_oc, J_sc, P_rad, and P_max represent the open circuit voltage, short circuit current density, incident light intensity and maximum power, respectively.

Results and Discussions

Performance of the SK-1150 unit

Figure 6 shows the differences in the short-circuit current (ΔI_{sc_stc}) between that determined by SK-1150 and that determined at a recognized calibration center for linear reference cells at STC plotted against the centroid wavelength (W_c). As shown in Figure 6, the ΔI_{sc_stc} was within ±1.5%.

Figure 6. Difference in the short-circuit current (ΔIsc_stc) between that determined by the PRISM SK-1150 unit and that determined at a calibration center for linear cells under STC plotted against the centroid wavelength of the spectral responsivity (Wc). PRISM, Programmable Reference cell system for Irradiance adjustment by Spectral Measurement; SK-1150, Spectral responsivity unit; STC, standard test conditions.

The spectral responsivity (S(λ, E_b)) determined for the two nonlinear cells (cells A and B), an organic thin film solar cell (OPV), and a dye-sensitized solar cell containing an ionic liquid electrolyte (DSC-B) are shown in Figure 7. The ΔI_{sc_stc} values determined for these cells are shown in Tables 3 and 4. Nonlinear cells are those in which the spectral responsivities change with the bias light intensity [8]. The S(λ, E_b) of both cells increased with an increase in the bias light intensity in a wavelength range over 500 nm, while the degree of increase was larger for cell B. The ΔI_{sc_stc} was 0.1% for cell A and −0.3% for cell B.

Table 3. ΔI_{sc_stc} determined for two nonlinear cells (Cell A and Cell B)

Cell	ΔIsc_stc (%)
A	0.1
B	−0.3

Table 4. ΔI_{sc_stc} determined for OPV and DSC-B

Cell	ΔIsc_stc (%)
DSC, dye-sensitized solar cells; OPV, organic thin film solar cell.
OPV	−1.1
DSC-B	−2.6

Figure 7. Spectral responsivity (S(λ, Eb)) determined for two nonlinear cells (cells A and B), OPV and DSC-B: (A) Cell A, (B) Cell B, (C) OPV, (D) DSC-B. DSC, dye-sensitized solar cells; OPV, organic thin film solar cell.

Unlike the nonlinear cells, the S(λ, E_b) of the OPV and DSC-B decreased with an increase in the bias light intensity at wavelengths under 650 nm. Similar results have been reported for DSCs by Hara et al. [29], Guo et al. [22] and Aoki et al. [3]. Hara et al. have suggested that this decrease in the spectral responsivity may be related to light absorption in the wavelength range of 400–500 nm caused by Failed to parse (MathML with SVG or PNG fallback (recommended for modern browsers and accessibility tools): Invalid response ("Math extension cannot connect to Restbase.") from server "https://test.scipedia.com:8081/localhost/v1/":): {\textstyle I_3^{-}}

accumulation in the vicinity of the electrode due to oxidation of I− and accelerated by bias light irradiation. Table 4 shows that ΔIsc_stc was −1.1% for the OPV and −2.6% for DSC-B.

The maximum deviation under STC for the PRISM system was set within 4%, as mentioned before. The ΔI_{sc_stc} values determined for the linear and nonlinear reference cells, OPV, and DSC were found to be within this maximum deviation.

Performance of the SRC-1100 device

First, the differences in the short-circuit current (ΔI_sc) between I_cal and I_mes calculated from equation (10) for the linear reference cells under STC were determined, and the results are shown in Figure 8. Two sets of the SRC-1100 device with different solar simulators (San-ei Electric XES-40S and Newport Corp 94023A) were employed. As shown in Figure 8, ΔI_sc was within ±3%, which is within the maximum deviation set for the PRISM system.

Figure 8. Difference in the short-circuit current (ΔIsc) between Ical and Imes calculated from equation (10) for the reference cells (Konica Minolta AK series and conventional reference cells made by other companies) under the solar simulators.

Next, the ΔI_sc of the nonlinear cells, OPV, and DSCs were determined by changing the irradiance. A San-ei Electric XES-40S solar simulator was used for the nonlinear cells and the OPV, and a Yamashita Denso YSS-T150A simulator was used for the DSCs. Figure 9 shows the ΔI_sc determined for these cells. The ΔI_sc of the nonlinear cells and the OPV was within ±4% and larger for cell B than cell A. The ΔI_sc of the DSCs was within ±3% and larger for DSC-A than DSC-B. The ΔI_sc determined for DSC-NIMS-1 and DSC-NIMS-2 were within ±4% under the solar simulator with an irradiance range of 10–1000 W/m². These results show that the ΔI_sc is within the maximum deviation set for the PRISM system even under such low irradiance as 10 W/m².

Figure 9. ΔIsc determined for two nonlinear cells (cells A and B), OPV, DSC-A and DSC-B under the solar simulator. OPV, organic thin film solar cell; DSC, dye-sensitized solar cells.

The ΔI_sc under LED was also investigated. The ΔI_sc for the reference cells under LED with an irradiance of 3.97 W/m² and that determined for nonlinear cells by changing the irradiance of LED are shown in Figure 10. The ΔI_sc of the reference cells was within ±4% which is within the maximum deviation set for the PRISM system. The ΔI_sc of the nonlinear cells was within ±3% when the irradiance was higher than 4 W/m². These results show that the PRISM system is applicable not only to sunlight but also LED light when the irradiance is higher than 4 W/m². Since an increase in ΔI_sc under low irradiance may result from the S/N ratio of the equipment, improvement in the equipment components will also need to be implemented for less uncertainty.

Figure 10. (A) ΔIsc determined for the reference cells under LED with an irradiance of 3.97 W/m2 and (B) ΔIsc determined for nonlinear cells by changing the irradiance of LED.

I–V characteristic measurements

Changes in solar cell efficiency and open circuit voltage upon irradiance with a light source

The PRISM system was applied to determine changes in the solar cell efficiency (η) and open circuit voltage (V_oc) upon irradiance with a solar simulator. The target cells were DSC-NIMS-2 and AK-100, and the solar simulator was a San-ei Electric XES-40S. Figure 11 shows the changes in η and V_oc upon irradiance with the solar simulator. The η of the DSC increased with an increase in irradiance at a range from 0.01 to about 0.2 sun, then gradually decreased, whereas the V_oc monotonously increased with an increase in irradiance. Contrarily, in the case of AK-100, both η and V_oc decreased with a monotonous decrease in irradiance. The rates of decrease in η and V_oc for the DSC with a decrease in irradiance were less than of those for AK-100.

Figure 11. Changes in the solar cell efficiency (η) and open circuit voltage (Voc) determined for DSC-NIMS-2 and AK-100 upon irradiance with a solar simulator. DSC-NIMS-2, dye-sensitized solar cells-National Institute for Materials Science.

Determination of solar cell efficiency under weak LED irradiation

The results shown in Figure 11 suggest that, under weak irradiation, higher performance can be expected for some types of solar cells when compared to crystalline solar cells. For example, organic solar cells can be specifically considered for indoor use due to their flexibility, lightness and high designability, however, a standard method to verify their performance has yet to be established.

The PRISM system was also applied to determine the photoelectric conversion efficiencies of OPV and DSC under LED which exhibits irradiance similar to indoor light. Table 5 shows the performance of the OPV under the solar simulator and LED. The solar cell efficiency (η) under LED was more than twice that obtained under 1 sun. Figure 12 shows the relationship between the spectral responsivity of the OPV and spectral irradiances of the light sources. As shown in Figure 12, the light emission wavelength region of the LED was approximately within the absorption wavelength region of the OPV, however, the wavelength region of natural sunlight is much wider than the absorption wavelength region of the OPV. This may explain why the η obtained under LED was greater than that obtained under 1 sun. The performance of DSC-NIMS-1 under the solar simulator and LED are shown in Table 6. As with the OPV, the η under LED was larger than that under 1 sun.

Table 5. Performance of OPV under a solar simulator (SAN-EI ELECTRIC XES-40S) and LED (Imac)

Light source	Jsc mA/cm2	Voc V	Pmax W/m2	Irradiance W/m2	η %
OPV, organic thin film solar cell.
Solar simulator	7.05	0.46	18.0	1000 (1 sun)	1.8
LED	0.0815	0.34	0.176	4.57	3.9

Table 6. Performance of DSC-NIMS-1 under a solar simulator (SAN-EI ELECTRIC XES-40S) and LED (Imac)

Light source	Jsc mA/cm2	Voc V	Pmax W/m2	Irradiance W/m2	η %
DSC-NIMS-1, dye-sensitized solar cells-National Institute for Materials Science.
Solar simulator	13.8	0.60	61.4	1000 (1 sun)	6.1
LED	0.120	0.47	0.345	4.10	8.4

Figure 12. Relationship between the spectral responsivity of the OPV (S(λ)) and spectral irradiance of the light sources ((E_LED(λ) for LED, E_ss(λ) for the San-ei Electric XES-40S (1 sun)). OPV, organic thin film solar cell.

Conclusions

The newly developed PRISM system, consisting of a SK-1150 unit which measures the absolute spectral responsivity of a target cell and the SRC-1100 device which stores this data along with the reference spectral irradiance and that of the light source in order to adjust its irradiance, was found to be applicable for any type of solar cell under various illumination conditions. Significantly, the SRC-1100 acts as the reference cell, allowing comparison studies without the preparation of conventional reference cells as defined in IEC 60904-2, 4, thus, dramatically reducing the preparation time for I–V characterization measurements of a newly developed cell. The PRISM system makes it unnecessary to prepare a filtered reference cell and then confirm its stability over months. It is thus possible to avoid these tedious and lengthy procedures before measurement of organic solar cell performance. This is because the data of the absolute spectral responsivity itself serves the same function as a reference cell.

Regarding accuracy, differences in the short-circuit current between that determined by the SK-1150 and at a recognized test center under STC were within ±2% for the filtered reference cells and nonlinear cells, and within ±3% for organic solar cells. The typical calibration uncertainty at a secondary or working calibration institute is around 2%, meaning that SK-1150′s accuracy is comparable to calibrations at these facilities. Upon irradiance adjustment with this PRISM system, the difference in the short-circuit current between that obtained by convolution of the absolute spectral responsivity with the spectral irradiance of a solar simulator or LED and that measured with the adjusted light source was within ±3% under STC and ±4% under various illumination conditions when the irradiance was higher than 4 W/m².

In the case of calibration of the light irradiance under STC conditions using a conventional method with a reference cell, the adjustment accuracy was also comparable the present PRISM method. However, in the case of the calibration of various kinds of light sources with even low irradiance, the PRISM system enables a traceable measurement method for irradiance adjustment which had so far been difficult due to the lack of a suitable reference cell with a certified value. This system will be particularly useful for the preparation and I–V measurement of nonlinear organic solar cells which have a variety of spectral responsivities.

Acknowledgments

The authors express their sincere appreciation to the Japan Science and Technology Agency (JST) Development of Advanced Measurement and Analysis Systems funding program for their financial support and encouragement. They thank Dr M. Yanagida of the National Institute for Materials Science for supplying the stable DSC cells used in this work. Sincere gratitude is also extended to the National Institute of Advanced Industrial Science & Technology (AIST, Japan), National Renewable Energy Laboratory (NREL, USA), and Physikalisch Technische Bundesanstalt (PTB, Germany) for their useful advice on the traceable calibration method.

Conflict of Interest

None declared.

References

1. Lee, M. M., J. Teuscher, T. Miyasaka, T. N. Murakami, and H. J. Snaith. 2012. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science338:643–647. doi: 10.1126/science.
2. Ito, S., H. Matsui, K. Okada, S. Kusano, T. Kitamura, Y. Wada, et al. 2004. Calibration of solar simulator for evaluation of dye-sensitized solar cells. Solar Energy Mater. Solar Cells82:421–429. doi: 10.1016/j.solmat.
3. Aoki, D., T. Aoki, H. Saito, S. Magaino, and K. Takagi. 2012. Methods for spectral responsivity measurements of dye-sensitized solar cells. Electrochemistry80:640–646. doi: 10.5796/electrochemistry.
4. Takagi, K., S. Magaino, H. Saito, T. Aoki, and D. Aoki. 2013. Measurements and evaluation of dye-sensitized solar cell performance. Photochem. Rev.14:1–12. doi: 10.1016/j.photochemrev.
5. Emery, K. A., and C. R. Osterwald. 1989. Solar cell calibration methods. Solar Cells27:445–453.
6. IEC 60904-22nd edition 2007–03: photovoltaic devices - part 2; Requirements for reference solar devices.
7. IEC 60904-41st edition 2009–06: photovoltaic devices - part 4; Reference solar devices - procedures for establishing calibration traceability.
8. IEC 60904-83rd edition 2014–05: photovoltaic devices - Part 8; Measurement of spectral responsivity of a photovoltaic (PV) device.
9. IEC 60904-32nd edition 2008–04: photovoltaic devices - Part 3; Measurement principles for terrestrial photovoltaic (PV) solar devices with reference spectral irradiance data.
10. Gevorgyan, S. A.2011. An inter-laboratory stability study of roll to roll flexible polymer solar modules. Sol. Energy Mater. Sol. Cells95:1398–1468.
11. Hinsch, A. 2013. Status of the dye solar cell technology (DSC) as a guideline for further research. Proceeding of the 28th European PV Solar Energy Conference and Exhibition 2013; 2239–2247.
12. Nishikawa, Y., K. Miyao, S. Tochimoto, K. Imai, and S. Winter. 2012a. The application of spectral reference cell to various photovoltaic cells. The Japan Society of Applied Physics Spring Meeting; March 2012: 16P-GP9-1.
13. Nishikawa, Y., K. Miyao, S. Tochimoto, K. Imai, and S. Winter. 2012b. The application of spectral reference cell to various photovoltaic cells. The Japan Society of Applied Physics Spring Meeting; March 2012: 16P-GP9-2.
14. Nishikawa, Y., K. Imai, S. Tochimoto, K. Miyao, and S. Winter. 2013. The application of spectral reference cells to non-linear photovoltaic cell. Konica Minolta Technol. Rep.10:81–87.
15. Uchida, S., and Y. Nishikawa. New evaluation method of photovoltaic by using spectral technology. International Conference on the Evaluation & Standardization of Organic Solar Cells 2013 (ICES2013); January 2013: IL3.
16. Nishikawa, Y. Organic photovoltaic evaluation method by utilizing spectral reference cell. Proceeding of the 93rd Annual Meeting of The Chemical Society of Japan; March 2013: 3H1-31.
17. Uchida, S., Y. Nishikawa, K. Miyao, K. Imai, S. Tochimoto, S. Magaino, et al. The new generations PV evaluation method by utilizing spectral technology. Proceeding of the 28th European PV Solar Energy Conference and Exhibition 2014; 3552-3556.
18. Uchida, S., Y. Nishikawa, K. Miyao, K. Imai, S. Tochimoto, S. Magaino, et al. The differential spectral responsivity (DSR) technology for evaluation of new generation PV. Proceeding of the 23rd International Photovoltaic Science and Engineering Conference; October 2013: 5-O-5.
19. Nishikawa, Y. New traceable evaluation method for organic photovoltaics. International Conference on the Evaluation & Standardization of Organic Solar Cells 2014 (ICES2014); February 2014: IL5.
20. ISO 15387: 2005 space systems - single-junction solar cells - measurement and calibration procedures.
21. Metzdorf, J., W. Möller, T. Wittchen, and D. Hünerhoff. 1991. Principle and application of differential spectroradiometry. Metrologia28:247–250.
22. Guo, X.-Z., Y.-H. Luo, Y.-D. Zhang, X.-C. Huang, D.-M. Li, and Q.-B. Meng. 2010. Study on the effect of measuring methods on incident photon-to-electron conversion efficiency of dye-sensitized solar cells by home-made setup. Rev. Sci. Instrum.81:103106.
23. JIS Z 8724: 1997 methods of color measurement - Light-source colour.
24. Sperfeld, P., D. Dzafic, F. Plag, F. Haas, C. Kröber, H. Albert, et al. Usability of compact array spectroradiometers for the traceable classification of pulsed solar simulators. Proceeding of the 27th European Photovoltaic Solar Energy Conference and Exhibition 2012; 3060–3065.
25. Habte, A., A. Andreas, L. Ottoson, C. Gueymard, G. Fedor, S. Fowle, et al. Indoor and outdoor spectroradiometer intercomparison for spectral irradiance measurement. Technical Report NREL/TP-5D00-61476. 2014: i–21.
26. Galleano, R., W. Zaaiman, P. Morabito, A. Minuto, A. Spena, S. Bartocci, et al. 2012. Intercomparison of spectroradiometers for solar spectral irradiance measurements. Preliminary results. AIP Conf. Proc.1477:139–142. doi: 10.1063/1.4753853.
27. Green, M. A., K. Emery, Y. Hishikawa, and W. Warta. 2009. Solar cell efficiency tables (Version 33). Prog. Photovoltaics Res. Appl.17:85–94.
28. Dirnberger, D., U. Kräling, H. Müllejans, E. Salis, K. Emery, Y. Hishikawa, et al. 2014. Progress in photovoltaic module calibration: results of a worldwide intercomparison between four reference laboratories. Meas. Sci. Technol.25:105005.
29. Hara, K., S. Igari, S. Takano, and G. Fujihashi. 2005. Characterization of photovoltaic performance of dye-sensitized solar cells. Electrochemistry73:887–896. doi: 10.5796/Electrochemistry.